Hot compression tests were conducted on a Gleeble-1500D thermal simulating tester.Based on the deformation behavior and microstructural evolution of superalloy GH79,different types of instability criteria of PRASAD,GEGEL,MALAS,MURTY and SEMIATIN were compared,and the physical significance of parameters was analyzed.Meanwhile,the processing maps with different instability criteria were obtained.It is shown that instability did not occur when average power dissipation rate was larger than 60%in the temperature range of 900-930°C and 960-1080°C,corresponding to the strain rate range of 5×10 -4 -1.8×10 -1 s -1 and 5×10 -4 -1.5×10 -1 s -1 ,respectively.The two domains are appropriate for the processing deformation of superalloy GH79.
The effect of hot compression on the grain boundary segregation and precipitation behavior of M6C carbide in theNi-20Cr-18W-1Mo superalloy was investigated by thermomechanical simulator, scanning electronic microscope （SEM） and X-raydiffraction （XRD）. Results indicate that the amount of M6C carbides obviously increases in the experimental alloy after hotcompression. Composition analyses reveal that secondary M6C carbides at grain boundaries are highly enriched in tungsten.Meanwhile, the secondary carbide size of compressive samples is 3？5 μm in 10% deformation degree, while the carbide size ofundeformed specimens is less than 1 μm under aging treatment at 900 and 1000 ℃. According to the thermodynamic calculationresults, the Gibbs free energy of γ-matrix and carbides decreases with increase of the compression temperature, and the W-rich M6Ccarbide is more stable than Cr-rich M23C6. Compared with the experimental results, it is found that compressive stress accelerates theW segregation rate in grain boundary region, and further rises the rapid growth of W-rich M6C as compared with the undeformedone.