Li3V2-2/3xMnx（PO4）3（0≤x≤0.12） powders were synthesized by sol-gel method. The effect of Mn2＋-doping on the structure and electrochemical performances of Li3V2（PO4）3/C was characterized by XRD, SEM, XPS, galvanostatic charge /discharge and electrochemical impedance spectroscopy（EIS）. The XRD study shows that a small amount of Mn2＋-doped does not alter the structure of Li3V2（PO4）3/C materials, and all Mn2＋-doped samples are of pure single phase with a monoclinic structure （space group P21/n）. The XPS analysis indicates that valences state of V and Mn are ＋3 and ＋2 in Li3V1.94Mn0.09（PO4）3/C, respectively, and the citric acid in raw materials was decomposed into carbon during calcination, and residual carbon exists in Li3V1.94Mn0.09（PO4）/C. The results of electrochemical measurements show that Mn2＋-doping can improve the cyclic stability and rate performance of these cathode materials. The Li3V1.94Mn0.09（PO4）3/C cathode material shows the best cyclic stability and rate performance. For example, at the discharge current density of 40 mA/g, after 100 cycles, the discharge capacity of Li3V1.94Mn0.09（PO4）3/C declines from initial 158.8 mA·h/g to 120.5 mA·h/g with a capacity retention of 75.9%; however, that of the Mn-undoed sample declines from 164.2 mA·h/g to 72.6 mA·h/g with a capacity retention of 44.2%. When the discharge current is increased up to 1C, the intial discharge capacity of Li3V1.94Mn0.09（PO4）3/C still reaches 146.4 mA·h/g, and the discharge capacity maintains at 107.5 mA·h/g after 100 cycles. The EIS measurement indicates that Mn2＋-doping with a appropriate amount of Mn2＋ decreases the charge transfer resistance, which is favorable for the insertion/extraction of Li＋.