Li3V2（PO4）3 precursor was obtained with V2Os.nH2O , LiOH＇H2O, NH4H2PO4 and sucrose as starting materials by grinding-sol-gel method, and then the monoclinic-typed Li3Vz（PO4）3 cathode material was prepared by sintering the amorphous Li3V2（PO4）3. The as-sintered samples were investigated by X-ray diffraction （XRD）, transmission electron microscopy （TEM）, N2 adsorption-desorption and electrochemical measurement. It is found that Li3Vz（PO4）3 sintered at 700 ℃ possesses good wormhole-like mesoporous structure with the largest specific surface area of 188 cmZ/g, and the smallest pore size of 9.3 nm. Electrochemical test reveals that the initial discharge capacity of the 700 ℃ sintered sample is 155.9 mA.h/g at the rate of 0.2C, and the capacity retains 154 mA.h/g after 50 cycles, exhibiting a stable discharge capacity at room temperature.